EUGMFR001 combines aluminium-oxide coated abrasive cloth with non-woven material in a burnishing roller. The hybrid construction is used to remove small scratches, refine the pattern and prepare a surface for a subsequent satin-finishing stage.
| Family code | EUGMFR001 |
|---|---|
| Tool type | Combination finishing roller |
| Construction | Coated abrasive cloth plus non-woven material |
| Abrasive | Aluminium oxide |
| Purpose | Scratch refinement and satin-finish preparation |
| Documented grits | 60 and 120 |
| Example dimensions | 100 mm diameter × 100 mm face width |
| Example arbor hole | 19 mm |
| Example maximum speed | 5,700 rpm |
Abrasive-cloth flaps and non-woven elements are combined in one industrial finishing roller. The coated abrasive provides cutting action while the non-woven component refines the emerging pattern.
The abrasive specified for the documented variants is aluminium oxide.
The roller is intended for burnishing machines and preparation before satin finishing. It is described for fine surface patterns and removal of small scratches.
It should be treated as a preparation tool: final appearance depends on the following finishing stage, grade sequence and workpiece direction.
One documented variant uses grit 60, a 19 mm arbor hole, 100 mm diameter and 100 mm face width. Its listed maximum speed is 5,700 rpm.
A grit 120 variant is also present in the family, allowing a finer preparation step with the same general roller concept.
Match bore and dimensions to the machine spindle and guard. Establish feed, overlap and contact pressure on test material before processing visible parts.
Do not exceed the marked speed. Replace a roller with damaged flaps, uneven wear or an insecure bore fit.
POLISHX technical profile · 2026-10-11 19:44:50