Struers methods: Plasma Spray Coatings Composite Layers Composite Layers 954 Susp P Lub. Source classification: Coatings.
Searchable text transcription
The page images and original PDF preserve the table layout and notation.
Grinding Steps PG FG FG 2 Surface Type SiC Foil #320 MD-Largo MD-Largo Disc speed (rpm) 300 150 150 Abrasive Type DP-Susp. P 9 µm DP-Susp. P 3 µm Predosing/dosing 3/6 3/6 Lubricant Type Water DP-Blue DP-Blue Predosing/dosing 3/6 3/6 Force (N) 25 40 35 Holder direction >> >> >> Holder speed (rpm) 150 150 150 Time (min) 1 6 5 Polishing Steps DP OP Surface Type MD-Dur MD-Chem Disc speed (rpm) 150 150 Abrasive Type DP-Susp. P 3 µm OP-U, 0.04 µm Predosing/dosing 3/6 1/10 Lubricant Type DP-Blue Predosing/dosing 3/10 Force (N) 25 10 Holder direction >> >< Holder speed (rpm) 150 150 Time (min) 4 1 Plasma Spray Coatings - Composite Layers - Composite Layers 954 Coatings Susp. P/Lub. The method is developed to fit a standard equipment configuration with 30 mm specimen on 300mm disc. Dosing levels are valid for following equipment: Tegramin, AbraPol and LaboPol For advice on how to adjust the method to fit your equipment, please take a look at Preparation Parameters. The preparation time for the plane grinding (PG) step depends very much on the condition of the samples and if they are prepared as single specimens or clamped in a specimen holder. Please check the samples after the first step and repeat it if necessary. Method comments Take a look at Preparation Parameters