Struers methods: Flakes 10 20 Hard Flakes In Any Matrix 1410 Susp Plub. Source classification: Composites and Reinforced Materials.
Searchable text transcription
The page images and original PDF preserve the table layout and notation.
Grinding Steps PG FG FG 2 FG 3 Surface Type MD-Piano 220 MD-Piano 500 MD-Piano 1200 MD-Largo Disc speed (rpm) 300 150 150 150 Abrasive Type DP-Susp. P 9 µm Predosing/dosing 3/6 Lubricant Type Water Water Water DP-Blue Predosing/dosing 3/6 Force (N) 40 40 40 40 Holder direction >> >> >> >> Holder speed (rpm) 150 150 150 150 Time (min) 2 3 3 7 Flakes - > 10-20 % hard flakes in any matrix 1410 Composites and Reinforced Materials Susp. P/Lub. Polishing Steps DP DP 2 Surface Type MD-Dac MD-Nap Disc speed (rpm) 150 150 Abrasive Type DP-Susp. P 3 µm DP-Susp. P 1 µm Predosing/dosing 3/6 3/6 Lubricant Type DP-Blue DP-Blue Predosing/dosing 3/10 3/14 Force (N) 35 30 Holder direction >> >> Holder speed (rpm) 150 150 Time (min) 6 3 The method is developed to fit a standard equipment configuration with 30 mm specimen on 300mm disc. Dosing levels are valid for following equipment: Tegramin, AbraPol and LaboPol For advice on how to adjust the method to fit your equipment, please take a look at Preparation Parameters. The preparation time for the plane grinding (PG) step depends very much on the condition of the samples and if they are prepared as single specimens or clamped in a specimen holder. Please check the samples after the first step and repeat it if necessary. Method comments Take a look at Preparation Parameters